What is bismuth oxid?
Bismuth oxid
The molecular formula of the inorganic compound is Bi2O3. The pure product comes in three types: a, b, and d. a type has a yellow monoclinic structure, relative densities of 8.9, melting points of 825, and is soluble only in acid. Hydrogen and hydrocarbons can reduce it easily to metallic Bismuth. It is a special material that has a cubic fluorite structure. The crystal lattice of d-Bi2O3 is void in 1/4, which gives it a high oxygen conductivity. Bismuth Oxide is mainly used for electronic ceramic powders. It can also be used as photoelectric materials, superconducting high temperature materials, and catalysts. Bismuth is an essential additive in electronic ceramic materials. Its purity must be at least 99.15%. Main application objects include ceramic capacitors, zinc oxide varistors, and ferrite magnet materials.
Bismuth Oxide preparation
1. Dropwise, add to the bismuth-nitrate solution at 80-90degC a sodium hydroxide-free aqueous mixture and mix. The solution stays alkaline and the white, volume-swelling, bismuth oxide hydroxide Bi(OH3) precipitates. This solution is heated, stirred and dehydrated to yellow. Bismuth trioxide . After filtering, drying and washing the bismuth oxide is obtained.
2. Mix them under a nitrogen-filled atmosphere by adding dropwise a 1,5 mol/L sodium hydroxide aqueous without carbon dioxide solution to a bismuth solution dissolved at 0.1 mol/L in 1 mol/L of nitric (at 80 to 90deg C). During precipitation, the solution remains alkaline. The white volume-expanded Bismuth Oxide Hydrate Bi(OH)3 does precipitate, but it dehydrates and turns into light yellow Bismuth Trioxide when stirred for some time in the hot water solution. Decant the solution and wash it 15 times without adding air or carbon dioxide. Then filter and dry.
3. The graphite electrode is placed between the metal surface and the graphite electrode. An arc is created under oxygen flow. For a continuous supply of oxygen to the crucible, it should be placed inside a large vessel. The reaction is carried out at 750-800degC and the b bismuth trioxide is generated quickly. It has a purity level of 99.8%. A high-temperature phase B-type product is obtained by quenching the product in water or a metal plate.
4. Stir vigorously as you add the acidic Bi(NO3)3*5H2O (20g dissolved 2mol/L in HNO3) solution to the excess sodium-carbonate solution. Filter, wash, and then dry the Bi2O3CO3 crystalline precipitate. Place it in an aluminium boat and heat the air in it at 650K over about 1.5 hours.
5. Burn the Bismuth Subnitrate between 400 and 500 to remove NO3-ions for around (34h).
2BiONO3=Bi2O3+NO+NO2+O2
After cooling down, the final product will be a lemon yellow color.
Bismuth Oxide is used in the application of Bismuth oxide
Bismuth oxide is used to prepare bismuth sal; it can also be used in electronic ceramic powder materials, photoelectric materials, superconductors at high temperatures, and as a catalyst. Bismuth Oxide is an essential additive in electronic ceramic materials and must have a purity of at least 99.15%. Main application objects include zinc oxide varistors; ceramic capacitors and ferrite magnet materials. Other applications include glaze rubber compounding, medicine, red glass compounding, etc.
(aka. Technology Co. Ltd., a trusted global chemical supplier & manufacture with over 12 year’s experience in providing super-high-quality chemicals & Nanomaterials. The Bismuth Oxide Powder produced by our company is high in purity, fine particle size and impurity content. Please. Contact Us if necessary.
Bismuth Oxide preparation
1. Dropwise, add to the bismuth-nitrate solution at 80-90degC a sodium hydroxide-free aqueous mixture and mix. The solution stays alkaline and the white, volume-swelling, bismuth oxide hydroxide Bi(OH3) precipitates. This solution is heated, stirred and dehydrated to yellow. Bismuth trioxide . After filtering, drying and washing the bismuth oxide is obtained.
2. Mix them under a nitrogen-filled atmosphere by adding dropwise a 1,5 mol/L sodium hydroxide aqueous without carbon dioxide solution to a bismuth solution dissolved at 0.1 mol/L in 1 mol/L of nitric (at 80 to 90deg C). During precipitation, the solution remains alkaline. The white volume-expanded Bismuth Oxide Hydrate Bi(OH)3 does precipitate, but it dehydrates and turns into light yellow Bismuth Trioxide when stirred for some time in the hot water solution. Decant the solution and wash it 15 times without adding air or carbon dioxide. Then filter and dry.
3. The graphite electrode is placed between the metal surface and the graphite electrode. An arc is created under oxygen flow. For a continuous supply of oxygen to the crucible, it should be placed inside a large vessel. The reaction is carried out at 750-800degC and the b bismuth trioxide is generated quickly. It has a purity level of 99.8%. A high-temperature phase B-type product is obtained by quenching the product in water or a metal plate.
4. Stir vigorously as you add the acidic Bi(NO3)3*5H2O (20g dissolved 2mol/L in HNO3) solution to the excess sodium-carbonate solution. Filter, wash, and then dry the Bi2O3CO3 crystalline precipitate. Place it in an aluminium boat and heat the air in it at 650K over about 1.5 hours.
5. Burn the Bismuth Subnitrate between 400 and 500 to remove NO3-ions for around (34h).
2BiONO3=Bi2O3+NO+NO2+O2
After cooling down, the final product will be a lemon yellow color.
Bismuth Oxide is used in the application of Bismuth oxide
Bismuth oxide is used to prepare bismuth sal; it can also be used in electronic ceramic powder materials, photoelectric materials, superconductors at high temperatures, and as a catalyst. Bismuth Oxide is an essential additive in electronic ceramic materials and must have a purity of at least 99.15%. Main application objects include zinc oxide varistors; ceramic capacitors and ferrite magnet materials. Other applications include glaze rubber compounding, medicine, red glass compounding, etc.
(aka. Technology Co. Ltd., a trusted global chemical supplier & manufacture with over 12 year’s experience in providing super-high-quality chemicals & Nanomaterials. The Bismuth Oxide Powder produced by our company is high in purity, fine particle size and impurity content. Please. Contact Us if necessary.